| Tidak. | Hartanah Resin | Nilai tipikal | Unit | Kaedah Ujian |
| 1 | Graviti Tentu, 23℃ | 1.05 | g/cm³ | ASTM D792 |
| 2 | Pengecutan Acuan, 23℃, 3.2mm, 23℃ | 0.4-0.7 | % | ASTM D955 |
| 3 | Kadar Aliran Lebur, 220℃, 10kg | 22 | g/10 minit | ASTM D1238 |
| 4 | Kekuatan Tegangan pada Asil, 23℃, 50mm/min, 3.2mm | 49 | MPa | ASTM D638 |
| 5 | Pemanjangan Tegangan pada Hasil, 23℃, 50mm/min, 3.2mm | 5 | %, (Minimum) | ASTM D638 |
| 6 | Pemanjangan Tegangan pada Putus, 23'℃, 50mm/min, 3.2mm | 10 | %, (Minimum) | ASTM D638 |
| 7 | Modulus Tegangan, 23℃, 50mm/min, 3.2mm | 2350 | MPa | ASTM D638 |
| 8 | Kekuatan Lenturan, 23℃, 15mm/min, 3.2mm | 78 | MPa | ASTM D790 |
| 9 | Modulus Fleksibel, 23℃, 15mm/min, 3.2mm | 2550 | MPa | ASTM D790 |
| 10 | Kekuatan Impak Izod, Bertakuk, 3.2mm, 23℃ | 220 | J/m | ASTM D256 |
| 11 | Kekuatan Impak Izod, Bertakuk, 3.2mm, -30℃ | 90 | J/m | ASTM D256 |
| 12 | Kekuatan Impak Izod, Bertakuk, 6.4mm, 23℃ | 220 | J/m | ASTM D256 |
| 13 | Kekuatan Impak Izod, Bertakuk, 6.4mm,-30℃ | 90 | J/m | ASTM D256 |
| 14 | Kekerasan Rockwell, Skala-R | 110 | / | ASTM D785 |
| 15 | HDT, Edgewise, 1.82MPa, 6.4mm, Tidak Disepuh | 85 | °C | ASTM D648 |
| 16 | VICAT, 50N, 50℃/j | 92 | °C | ASTM D1525 |
| 17 | RTI Electrical | 95 | °C | UL 746B |
| 18 | Mekanikal RTI dengan Impak | 95 | °C | UL 746B |
| 19 | Mekanikal RTI tanpa Impak | 95 | °C | UL 746B |
| 20 | Kemudahbakaran, 1.5mm | HB | / | UL 94 |
| 21 | Kemudahbakaran, 3.0mm | HB | / | UL 94 |